The role of surface depletion layer effects on the enhancement of the UV emission in ZnO induced by a nanostructured Al surface coating

Download (5.58 kB)
preprint
posted on 2023-11-30, 18:51 authored by Saskia Fiedler, Laurent O. Lee Cheong Lem, Cuong Ton-That, Matthew R. Phillips
The UV enhancement of Al-coated ZnO single crystals with a wide range of carrier densities is systematically studied using depth-resolved cathodoluminescence (CL) and photoluminescence (PL) as well as valence band X-ray photoemission spectroscopy (VB-XPS). AN up to 17-fold enhanced PL UV emission for Al-coated ZnO with the highest carrier density (2 x 10^17 cm^-3) was measured, which falls to a 12-fold increase for the lowest carrier density (3 x 10^13 cm^-3). Depth-resolved CL measurements confirm that the enhancement is strongest near the metal coating-ZnO interface consistent with an increased UV emission due to an exciton-localized surface plasmon coupling mechanism. Correlative CL, PL and VB-XPS studies reveal that a number of additional effects to the presence of the Al surface coating also contribute to the UV enhancement factor. These include increased UV enhancement due to the formation of a surface depletion layer induced by the metal surface coating, which also passivates competitive non-radiative surface recombination channels found in uncoated ZnO. Significantly, it was established that the magnitude of the emission enhancement factor can be raised in a controlled way by reducing the thickness of the depletion layer by increasing the carrier density. The contribution of these effects collectively provides an explanation for the large span of enhancement factors reported in the literature.

History

Disclaimer

This arXiv metadata record was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.

Usage metrics

    Categories

    Licence

    Exports

    RefWorks
    BibTeX
    Ref. manager
    Endnote
    DataCite
    NLM
    DC